304L Stainless Steel Plate

Name: 304L Stainless Steel Plate
SKU: 0

304L stainless steel is remarkably similar to 304 stainless steel in their chemical composition. but there is one key difference. In grade 304 stainless steel, the maximum carbon content is set at 0.08%, whereas grade 304L stainless steel has a maximum carbon content of 0.03%. This is why the “L” in 304L can be interpreted as extra-low carbon.

Phone ：+86 18888888888

WhatsApp : +86 18888888888

Email : admin@admin.com

Contact Us

Product Description

304L stainless steel plate is a variant of 304 stainless steel plate with a lower carbon content and is used where welding is required. The lower carbon content minimizes the precipitation of carbides in the heat-affected zone close to the weld, and the precipitation of carbides may cause intergranular corrosion of stainless steel in certain environments. Basically, using 304L eliminates the need to anneal weld joints prior to using the completed metal form, saving time and effort. Generally speaking, both 304 and 304L stainless steel plates can be used for many of the same applications. The differences are often minor enough that one isn’t considered massively more useful over the other. 304L stainless steel plate is widely used in fields such as food processing equipment, building materials, automobile parts.

Product Parameters

Product Name	304L Stainless Steel Plate
Type	Plate
Thickness	0.3mm-200mm
Length	2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.
Width	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Scope of Application	Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging,Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.
Certificate	ISO, SGS, BV, etc.
Production Technology	Hot Rolling, Cold Rolling
Edge Processing	Edging, Trimming

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.03	≤1.0	≤ 2.0	18.0～20.0	8.0～12.0	≤ 0.03	≤ 0.035

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥ 520	≥ 205	≥ 40	≤ 187HB ;≤ 90HRB;≤ 200HV

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
8.03	193	16.9	16.2	72

Product Display

Factory Display

FAQ

1.What kind of customer service do you provide?

We provide comprehensive customer service, including basic design, procurement of supporting facilities, and options for dispatching installation guides.

2.What are the customer evaluations of your company?

We are proud to consistently receive five-star reviews from our customers, which demonstrates our commitment to quality and service.

3.What is your quality inspection process like?

Our strict quality inspection process ensures that every product meets the highest standards of excellence. From raw materials to finished products, every stage is carefully inspected to ensure excellent quality.

4.Do you accept container loading inspection?

Welcome to dispatch inspectors, not only for container loading, but also at any time during production.

5.What is the delivery time?

The delivery time depends on the quantity of orders. Usually, the delivery time to the nearest port in China is 15-30 days after receiving the deposit.

6. How to obtain a project quotation?

You can contact us 24 * 7 via email, phone, WhatsApp, WeChat, etc. You will receive a reply within 4 hours.

Product recommendation